Technical Parameters:

Content (%): >99.9

Average particle size: 30nm

Specific surface area: 35m2/g

Particle morphology: irregular

Appearance: blue powder

Bulk density: 0.83g/cm3

Tap density: 7.14 g/cm3

The product is based on the characteristics of nano-ATO, doped with other metal oxides to produce a modified ATO nano-paste with superior thermal insulation properties. This modified ATO nano-insulation medium has both nano-ATO transparency. In addition to physical properties such as heat insulation, it also differs from the characteristics of nano-ATO. In particular, the ability to block IR in the near-infrared region with a wavelength below 1000 nm is much greater than the barrier capability of ATO and ITO for IR, and is superior to near-infrared rays below 1000 nm. Barrier ability. The area most sensitive to the thermal sensation of human skin is the near-infrared region below 1000 nm. Therefore, the use of such an insulating medium to prepare various automotive glass, architectural glass sunscreen thermal insulation film or glass sunscreen thermal insulation coating can greatly Improve the comfort of the human body, save energy, achieve more effective winter and cool in summer, and provide technical guarantee for creating a more comfortable, environmentally friendly and energy-saving indoor environment. This technology fills the gaps in the domestic and international markets.

Product Features：

Appearance: blue liquid

Particle size: less than 40nm

Solid content: 16%

IRR≥99%

UVR≥99%

VLT≥99%

Optical effect: It has an excellent barrier capability for near-infrared (IR) below 1000 nm, which can greatly improve the thermal insulation performance. Solvent: It may be MEK, EA, MIBK, DIBK, xylene, and the like. It can also be aqueous (except alcohol).

Dispersibility: It can be used in various acrylic, polyester, silicone and other resin systems.

Precautions for use: Pay attention to the ambient humidity when opening the bottle. It is not recommended if the ambient humidity exceeds 65%.

Instructions:

It may be directly added to the corresponding resin system, and may be added to a nano-slurry system of other metal oxides such as ATO and ITO. Recommended amount: 5%-20%

Application areas:

Manufacture of a variety of transparent sunscreen insulation films to create a variety of transparent glass sunscreen insulation coatings.

Effective storage time: 180 days (humidity is less than 60% environmental preservation).

Storage temperature: 5-25 ° C.

Storage in a dry environment can extend the storage time.